Silgado, Jimy UnfriedNaranjo Vásquez, Luis JoséRuíz Tenorio, Isabela2020-12-222020-12-222020-12-19https://repositorio.unicordoba.edu.co/handle/ucordoba/3840In this monograph, the effect that the heat input generated by fusion welding processes in high-strength and low-alloy steels has been studied on the microstructure and on the fracture toughness and impact resistance. A bibliographic review including articles, research works and scientific reports was carried out where these steels were welded with different processes and / or the thermal cycles suffered by a welded joint were simulated through thermal treatments and software that recreated these conditions. Afterwards, by means of optical microscopy tests, scanning electron microscopy, hardness and microhardness tests, Charpy impact resistance tests and CTOD fracture toughness tests, among other techniques the steels were characterized and evaluated on the welded zones and sub-zones, in especially the heat affected zone of the base metal, where the greatest variation of microconstituents was concentrated. According to the results, it was determined that the toughness and the fracture behavior are subject to microstructural changes due to the heat input from the welding processesRESUMEN .......................................................................................................................... 14ABSTRACT ........................................................................................................................ 151. INTRODUCCIÓN .......................................................................................................... 162. OBJETIVOS ................................................................................................................... 192.1 OBJETIVO GENERAL ........................................................................................... 192.2 OBJETIVOS ESPECÍFICOS .................................................................................. 193. DESARROLLO DEL TEMA ........................................................................................ 203.1 Determinar mediante la revisión bibliográfica los cambios microestructurales debido al aporte térmico por los procesos de soldadura en los aceros de alta resistencia y baja aleación .............................................................................................. 203.2. Analizar los resultados obtenidos en estudios consultados sobre el efecto del proceso de soldadura en las propiedades mecánicas de tenacidad al impacto y tenacidad a la fractura en aceros de alta resistencia y alta aleación ......................... 463.3. Correlacionar la entrada de calor con los resultados de cambios microestructurales con tendencias y tipos de fractura encontrados en aceros de alta resistencia y baja aleación soldados .............................................................................. 804. CONCLUSIONES ....................................................................................................... 905. REFERENCIAS .......................................................................................................... 91application/pdfspaCopyright Universidad de Córdoba, 2020Influencia de la entrada de calor por procesos de soldadura en la tenacidad y resistencia a la fractura de aceros de alta resistencia y baja aleaciónTrabajo de grado - Pregradoinfo:eu-repo/semantics/openAccessAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)MicroestructuraResistencia al impactoTenacidad a la fracturaEntrada de calorZona afectada por el calorAceros de alta resistencia y baja aleaciónMicrostructureImpact resistanceFracture toughnessHeat inputHeat affected zoneHigh strength and low alloy steels