Unfried Silgado, JimyZambrano Rodríguez, HabibHerrera de Oro, Edinson de Jesús2023-02-272023-02-272022-02-27https://repositorio.unicordoba.edu.co/handle/ucordoba/7230The effect of the heat input generated by the GMAW welding process and protective gas 90Ar10CO2 on the fracture toughness of the different welding zones in the joints of ASTM A572 Gr 50 steel, which is a high-quality steel, was evaluated. High strength and low alloy (HSLA). Initially, the characterization of the base metal was carried out through techniques such as: optical emission spectrometry, optical microscopy, tensile tests, hardness tests and fracture toughness tests, with these data on chemical composition, microstructure, stress creep, hardness and fracture toughness values, respectively. Subsequently, the welding of the 400mmX150mmX6,35mm steel plates was carried out, by means of GMAW, using different heat inputs (high and low). From the welding coupons, the different welding zones were identified by macrography; and the phases in said zones were identified by means of metallography and X-ray diffraction. Then the fracture toughness test was carried out on specimens with the pre-crack located in the thermally affected zone (HAZ) and in the weld metal zone, welded joints. It was evidence that the fracture toughness is correlated with the microstructural changes in the ASTM A572 Gr 50 steel product of the thermal inputs of the GMAW welding process, this has an impact on the resulting phases; as well as the size, location and composition of the precipitates.RESUMEN .................................................................................................. 1ABSTRACT ................................................................................................ 21. Capítulo I. Descripción del Trabajo de Investigación ....................... 31.1. Introducción .................................................................................................................. 31.2. Objetivos ....................................................................................................................... 51.2.1. Objetivo general ..................................................................................................... 51.2.2. Objetivos específicos ............................................................................................. 51.3. Estructura de la tesis ..................................................................................................... 61.4. Revisión de literatura ..................................................................................................... 71.4.1. Marco Conceptual .................................................................................................. 71.4.1.1. Aceros HSLA .................................................................................................. 71.4.1.2. Acero ASTM A572 Gr 50 ................................................................................. 71.4.1.3. Proceso de Soldadura GMAW ........................................................................ 91.4.1.4. Proceso de Soldadura GMAW ........................................................................ 91.4.2. Estado del arte ..................................................................................................... 151.5. Trabajos derivados ...................................................................................................... 182. Capítulo II. Diseño Experimental ..................................................... 192.1. Universo ...................................................................................................................... 192.2. Variables ..................................................................................................................... 192.3. Recolección de datos .................................................................................................. 202.4. Determinación del número de probetas ....................................................................... 223. Capítulo III. Caracterización Inicial .................................................. 243.1. Introducción ................................................................................................................ 243.2. Materiales y Métodos .................................................................................................. 243.2.1. Caracterización Microestructural del Metal Base .................................................. 243.2.2. Determinación de fases presentes por Difracción de Rayos X ............................. 253.2.3. Determinación de la Composición Química .......................................................... 253.2.4. Caracterización Mecánica .................................................................................... 253.2.4.1. Ensayos de Tracción ..................................................................................... 253.2.4.2. Mediciones de Microdureza .......................................................................... 263.3. Resultados .................................................................................................................. 273.3.1. Caracterización Microestructural del Metal Base .................................................. 273.3.2. Determinación de fases presentes por Difracción de Rayos X ............................. 313.3.3. Determinación de la Composición Química .......................................................... 323.3.4. Caracterización Mecánica .................................................................................... 323.3.4.1. Ensayos de Tracción ..................................................................................... 323.3.4.2. Mediciones de Microdureza .......................................................................... 343.4. Conclusiones............................................................................................................... 354. Capítulo IV. Obtención de Juntas Soldadas ................................... 364.1. Introducción ................................................................................................................ 364.2. Materiales y métodos .................................................................................................. 364.2.1. Diseño de la junta ................................................................................................ 364.2.2. Parámetros de soldadura ..................................................................................... 364.2.3. Obtención de juntas soldadas .............................................................................. 374.2.4. Caracterización de las juntas soldadas ................................................................ 384.2.4.1. Macrografías de las juntas soldadas ............................................................. 384.2.4.2. Determinación del porcentaje de dilución ...................................................... 384.2.4.3 Micrografías de las juntas soldadas .............................................................. 384.2.4.4. Determinación de fases por Difracción de Rayos X (DRX) ............................ 384.2.4.5. Mediciones de microdureza .......................................................................... 384.2.4.6. Ensayos de tracción en juntas soldadas ....................................................... 394.3. Resultados .................................................................................................................. 404.3.1. Diseño de la junta ................................................................................................ 404.3.2. Parámetros de soldadura ..................................................................................... 414.3.3. Obtención de juntas soldadas .............................................................................. 424.3.4. Caracterización de las juntas soldadas ................................................................ 434.3.4.1. Macrografías de las juntas soldadas ............................................................. 434.3.4.2. Determinación del porcentaje de dilución ...................................................... 454.3.4.3. Micrografías de las juntas soldadas .............................................................. 464.3.4.4. Determinación de fases por Difracción de Rayos X (DRX) ............................ 494.3.4.5. Mediciones de microdureza .......................................................................... 504.3.4.6. Ensayos de tracción en juntas soldadas ....................................................... 514.4. Conclusiones............................................................................................................... 535. Capítulo V. Medición de Tenacidad a la Fractura ........................... 545.1. Introducción ................................................................................................................ 545.2. Materiales y métodos .................................................................................................. 545.2.1. Especímenes de prueba ...................................................................................... 545.2.2. Ensayos de Tenacidad a la Fractura .................................................................... 565.3. Resultados .................................................................................................................. 595.3.1. Ensayos de Tenacidad a la Fractura .................................................................... 595.3.1.1. Metal base .................................................................................................... 595.3.1.2. Juntas soldadas con entrada de calor alta .................................................... 655.3.1.3. Juntas soldadas con entrada de calor baja ................................................... 705.4. Conclusiones............................................................................................................... 766. Capítulo VI: Análisis Estadístico de las mediciones de tenacidad a la fractura................................................................................................. 776.1. Análisis Estadístico ..................................................................................................... 776.2. Conclusiones............................................................................................................... 817. Conclusiones Generales y Futuros Trabajos ................................. 827.1. Objetivo específico I: ................................................................................................... 827.2. Objetivo específico II: .................................................................................................. 827.3. Objetivo específico III: ................................................................................................. 827.4. Futuros trabajos. ......................................................................................................... 828. Bibliografía ........................................................................................ 83application/pdfspaCopyright Universidad de Córdoba, 2023Trabajo de grado - Maestríainfo:eu-repo/semantics/openAccessAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)HSLAGMAWZATCaracterizaciónTenacidadFracturaHSLAGMAWZATCharacterizationToughnessFracture