González Doria, Yahir EnriqueMiranda Cantillo, César AugustoQuintero Torres, Jason2020-10-282020-10-282020-10-28https://repositorio.unicordoba.edu.co/handle/ucordoba/3474This research paper carried out thermal conductivity measurement tests in accordance with ASTM C 177 (2013). Blocks were composed of mortar, bovine manure and coconut fiber where the bovine manure was adjusted by a maximum of 10% and 1,5% coconut fiber of the total volume of sand used in the block. Subsequently, compression resistance tests were performed and the percentage of moisture absorption and density was evaluated under ASTM C140. First of all, the individual amounts that make up a block in terms of cement, water and sand were calculated. An experimental design determined the quantities of specimens to be manufactured between blocks and plates for thermal conductivity assessment. For the preparation of the materials, a process of crushing and drying the manure as well as drying to the coconut fiber was carried out. Then the manufacture of the blocks and plates under the above-mentioned standards was completed. The results obtained were that manure reduced the coefficient of thermal conductivity by 50% when replaced by 10% and 1,5% coconut fiber with respect to a control plate. In terms of coconut fiber with percentages of 0,5; 1 and 1,5%, they gave greater compression resistance results than a control block (block containing no material other than its natural composition). It is worth noting the blocks with percentages of coconut fiber 0,5%, coconut fiber 1%, coconut fiber 1,5% and bovine manure 3% with coconut fiber 1,5% meet the compression resistance requirements set out in ASTM C129-171. INTRODUCCIÓN ............................................................................................................... 172. OBJETIVOS ........................................................................................................................ 192.1. Objetivo general ........................................................................................................... 192.2. Objetivos específicos.................................................................................................... 193. MARCO TEÓRICO............................................................................................................. 203.1. CONDUCTIVIDAD TÉRMICA .......................................................................................... 203.2. AISLANTE TÉRMICO ...................................................................................................... 223.3. CONDUCTOR TÉRMICO ................................................................................................ 233.4. MÉTODOS DE MEDICIÓN DE CONDUCTIVIDAD TÉRMICA ........................................... 233.4.1. Método de cajas de estado estacionario ............................................................. 243.4.2. Método de placa caliente en estado estable ....................................................... 243.4.3. Método de alambre caliente transitorio .............................................................. 253.4.4. Método de fuente de plano transitorio ............................................................... 263.5. RESIDUOS ORGÁNICOS ................................................................................................ 273.6. COCO ............................................................................................................................ 273.7. FIBRAS NATURALES ...................................................................................................... 283.8. FIBRAS DEL MESOCARPIO DEL COCO ........................................................................... 293.9. ESTIÉRCOL .................................................................................................................... 303.10. DENSIDAD .................................................................................................................... 313.11. MORTERO ..................................................................................................................... 313.12. CEMENTO ..................................................................................................................... 313.13. AGREGADOS O ÁRIDOS ................................................................................................ 323.14. CLASIFICACIÓN DE LOS AGREGADOS SEGÚN SU TAMAÑO ......................................... 323.15. RESISTENCIA EN MORTEROS ........................................................................................ 333.16. BLOQUE DE CONSTRUCCIÓN ....................................................................................... 353.17. BLOQUES VIBRO COMPACTADOS ................................................................................ 373.18. ENSAYO A COMPRESIÓN PARA BLOQUES VIBRO COMPACTADOS .............................. 383.19. ESPECTROSCOPÍA INFRARROJA POR TRANSFORMADA DE FOURIER (FTIR) ................ 383.20. DIFRACCIÓN DE RAYOS X (DRX) ................................................................................... 393.21. MICROSCOPIA ELECTRÓNICA DE BARRIDO (SEM) ....................................................... 394. MATERIALES Y MÉTODOS ............................................................................................ 444.1. OBTENCIÓN DEL MESOCARPIO DEL COCO (FIBRA DE COCO). ..................................... 444.2. OBTENCIÓN DEL ESTIÉRCOL BOVINO........................................................................... 454.3. CARACTERIZACIÓN FÍSICO QUÍMICA DE LOS MATERIALES. ......................................... 464.3.1. Análisis próximo de la fibra de coco y del estiércol bovino. ................................ 464.3.2. Análisis elemental de la fibra de coco y estiércol bovino. ................................... 474.3.3. Espectroscopia infrarroja por transformada de Fourier (FTIR). ........................... 474.3.4. Difracción de rayos X (DRX).................................................................................. 484.3.5. Microscopia electrónica de barrido (SEM). .......................................................... 484.3.6. Densidad de la fibra de coco y del estiércol bovino. ........................................... 484.4. PREPARACIÓN DE LOS RESIDUOS ORGÁNICOS UTILIZADOS PARA LA FABRICACIÓN DE BLOQUES Y PROBETAS. ............................................................................................................ 534.5. ARENA Y CEMENTO ...................................................................................................... 544.6. ELABORACIÓN DE LOS BLOQUES VIBRO COMPACTADOS Y PROBETAS PARA ENSAYOS DE CONDUCTIVIDAD TÉRMICA. ............................................................................................... 554.7. ENSAYOS REALIZADOS A LOS BLOQUES Y PROBETAS PARA ENSAYOS DE CONDUCTIVIDAD TÉRMICA. ..................................................................................................... 604.7.1. Estudio de conductividad térmica a las probetas. ............................................... 604.7.2. Ensayos de compresión a bloques vibro compactados. ...................................... 625. RESULTADOS Y DISCUSIÓN ......................................................................................... 655.1. RESULTADOS DE LA CARACTERIZACIÓN FÍSICO QUÍMICA DE LOS MATERIALES. ........ 655.1.1. Resultados del análisis próximo de los materiales. ............................................. 655.1.2. Resultados del análisis elemental de los materiales. ........................................... 665.1.3. Análisis por microscopia óptica ........................................................................... 675.1.4. Espectroscopia infrarroja por transformada de Fourier (FTIR). ........................... 685.1.5. Microscopia electrónica de barrido (SEM). .......................................................... 725.1.6. Densidad de los materiales .................................................................................. 745.1.7. Resultados del analisis de la arena y el cemento ................................................. 745.1.8. Elaboración de bloques y probetas para la medición de conductividad térmica 755.2. ENSAYOS REALIZADOS A LOS BLOQUES Y PROBETAS PARA LA CONDUCTIVIDAD TÉRMICA................................................................................................................................... 755.2.1. Resultados de conductividad térmica a las probetas conforme a la norma ASTM C177-19 755.2.2. Resultados de resistencia a la compresión de los bloques vibro compactados conforme a la norma ASTM C140 ........................................................................................ 776. CONCLUSIÓN .................................................................................................................... 817. RECOMENDACIONES ...................................................................................................... 838. REFERENCIAS ................................................................................................................... 849. ANEXOS ............................................................................................................................. 91application/pdfspaCopyright Universidad de Córdoba, 2020Trabajo de grado - Pregradoinfo:eu-repo/semantics/restrictedAccessAtribución-NoComercial 4.0 Internacional (CC BY-NC 4.0)Estiércol bovinoMesocarpio del cocoBloques de mamposteríaResistencia a la compresiónConductividad térmicaBovine manureCoconut mesocarpMasonry blocksResistance to compressionThermal